Product information "Epoxy Resin L + Hardener S (15 min)"

Epoxy resin L + hardener S (15 minutes), working pack

- Thin-liquid, solvent- and filler-free

- Fast infusion of glass, aramid and carbon fibres

- High static and dynamic strength

Due to the low surface tension, the good adhesion and the low curing loss, it is very suitable for bonding of wood, metal and HARD PS foams such as styrofoam. It can be processed in all common processes such as hand lamination, pressure and vacuum impregnation as well as presses and windings.

Epoxy resin L has similar mechanical properties with the  hardener S as the laminating systems used in aircraft construction.

Processing time: 15 minutes (100 g / 20 °C)

Mixing ratio:100 : 40
 parts by weight Epoxy resin L : Hardener S
100 : 45
 Volume parts Epoxy resin L : Hardener S

Curing time: 24 hours
cold curing
,hardens from 5 °C (low temperature hardener)
Heat resistance:
 approx. 65 °C.

Material characteristics (pure resin hardened)  Epoxy resin L with hardener S:

Bending strength DIN EN ISO 178 in MPa

110

Bending E-module DIN EN ISO 178 in MPa

--

Tensile strength DIN EN ISO 527 in MPa

68

compressive strength DIN EN ISO 14126 in MPA

116

Initial viscosity ISO 3219 in mPas

880

CYTOX-certificate on the resin system epoxy resin L + hardener S  (see below under additional information):  this system is non-cytotoxic  (cell-damaging), important for applications in medical technology.

Related links to "Epoxy Resin L + Hardener S (15 min)"
Read, write and discuss reviews... more
Customer evaluation for "Epoxy Resin L + Hardener S (15 min)"
Write an evaluation
Evaluations will be activated after verification.

The fields marked with * are required.

Viewed